| 摘要： |
The fabricating process of Well-known Bellcore poly(vinylidene fluoride-hexaflutrropropyleoe) (PVcIF-HFP)-based polyrner, electrolytes is very complicated, tedious, and expensive owing to containing a large amount of fluorine substituents. Herein, a novel kind of poly(vinylene carbonate) (PVCA)-based polymer electrolyte is developed via a facile in situ polymerization method, which possesses the merits of good interfacial compatibility with electrodes. In addition, this polymer electrolyte presents a high ionic conductivity of 5.59 X 10(-4) S Cm-1 and a wide electrochemical stability window exceeding 4.8 V vs Li+/Li at ambient temperature. In addition, the rigid cyclic carbonate backbone of poly(vinylene carbonate) endows polymer electrolyte a superior mechanical property. The LiFe0.2Mn0.8PO4/graphite lithium ion batteries using this polymer electrolyte deliver good rate capability and excellent cyclability at room temperature. The superior performance demonstrates that the PVCA-based electrolyte via in situ polymerization is a potential alternative polymer elettrolyte for high-performance rechargeable lithium ion batteries. |