A nitrosation-reduction method had been applied for the modification of DCE-4 h. It was a kind of non-polar hypercrosslinked resin and synthesized by our group. The functional resin, NR-07, exhibited good adsorption performance for NACs (Nitroaromatics). The adsorption capacity of NR-07 for p-nitrobenzoic acid was almost 1.3 times as much as that of H-103 in 24 h. The adsorption rate of NR-07 calculated by the kinetic function was 1.6 times as much as that of DCE-4 h. According to the EA analysis and IR spectrum, the amine and carbonyl group were introduced onto the polymer chains of NR-07. These hydrophilic chemical groups of NR-07 contributed to a higher liquid-film diffusion rate than that of DCE-4 h. Besides, the pore volume within 0.46 similar to 4.3 nm increased after the modification process, which had a positive effect on the intra-particle diffusion process. |